Pengaruh suhu pemudaan baja paduan perkakas SKD11 modifikasi dalam rangka pembuatan cetakan ekstrusi (extrusion dies)
Info Katalog
File Repositori
Penerbit : FTI - Usakti
Kota Terbit : Jakarta
Tahun Terbit : 2004
Pembimbing 1 : Rosfian A.D.
Subyek : Mechanical engineering - steel
Kata Kunci : temperature effect, steel aging, tool alloy, SKD11, modification, extrusion dies
Status Posting : Published
Status : Tidak Lengkap
File Repositori
| No. | Nama File | Hal. | Link |
|---|---|---|---|
| 1. | 2004_TA_STM_06198110_Halaman-Judul.pdf | ||
| 2. | 2004_TA_STM_06198110_Lembar-Pengesahan.pdf | ||
| 3. | 2004_TA_STM_06198110_Bab-1_Pendahuluan.pdf | ||
| 4. | 2004_TA_STM_06198110_Bab-2_Tinjauan-Pustaka.pdf |
|
|
| 5. | 2004_TA_STM_06198110_Bab-3_Studi-Lapangan-dan-Penelitian.pdf |
|
|
| 6. | 2004_TA_STM_06198110_Bab-4_Proses-Penelitian-dan-Pengujian---Copy.pdf |
|
|
| 7. | 2004_TA_STM_06198110_Bab-5_Analisa-Hasil-Penelitian.pdf |
|
|
| 8. | 2004_TA_STM_06198110_Bab-6_Kesimpulan-dan-Saran.pdf | ||
| 9. | 2004_TA_STM_06198110_Daftar-Pustaka.pdf | ||
| 10. | 2004_TA_STM_06198110_Lampiran.pdf |
|
P Persaingan industri baja dewasa ini cenderung lebih kompetitif. Untuk itu dituntut kualitas baja yang tinggi, yaitu yang mempunyai kekuatan, kekenyalan, kekerasan dan lain-lain. Untuk memenuhi hal itu, salah satu caranya adalah dengan dilakukannya perlakuan panas yang bertujuan untuk mendapatkan kualitas dan sifat mekanis baja yang sesuai dengan yang diharaplcan. Proses perlakuan panas ini terdiri dari pengerasan dan pemudaan. Pada baja paduan SKD11 Mod, proses yang akan dilalui pada tahap awal adalah proses proses pengerasan yang didahului dengan preheating 1 pada suhu 650°C selama 30 menit, lalu preheating 2 pada suhu 850°C selama 30 menit kemudian suhu dinaikkan hingga titik austenisasi pada suhu 1030°C ditahan selama 60 menit lalu didinginkan dalam media udara selama 10 menit. Dilanjutkan menuju proses pemudaan dengan suhu 300°C, 550°C, 600°C dengan waktu penahanan 60 menit. Diharapkan dengan penelitian ini dapat mengetahui sifat-sifat mekanis dan memperbaiki karakteristik baja yang dibutuhkan dalam hal ini bahan pembuat cetakan ekstrusi dengan nilai keras yang disyaratkan (60) HRc
T Today's steel industry competition tends to be more competitive. For this reason, high quality steel is required, namely those that have strength, elasticity, hardness and others. To fulfill this, one way is to carry out heat treatment which aims to obtain the quality and mechanical properties of steel that are in accordance with what is expected. This heat treatment process consists of hardening and aging. In SKD11 Mod alloy steel, the process that will be passed in the initial stage is the hardening process which is preceded by preheating 1 at a temperature of 650°C for 30 minutes, then preheating 2 at a temperature of 850°C for 30 minutes then the temperature is raised to the austenitization point at a temperature of 1030°C held for 60 minutes then cooled in air for 10 minutes. Continued to the aging process with a temperature of 300°C, 550°C, 600°C with a holding time of 60 minutes. It is hoped that this research will be able to determine the mechanical properties and improve the characteristics of the steel required, in this case the material for making extrusion molds with the required hardness value (60) HRc.